ALLOYS
Gerry
Gerry

 

types

duroloy pc/abs grades

overview

types

  • PC/ABS - BLOW MOLDING
  • pc/abs - high impact
  • pc/abs - easy  flow
  • pc/abs - weather resistant
  • pc/abs - heat resistant                                                                       
  • pc/abs - fr
  • pc/abs - fr - non halogen
  • pc/abs - gf
  • pc/asa
  • Abs/pbt - high impact
  • abs/pbt - blow molding
  • abs/pbt - fr
  • abs/pbt - gf
  • ABS/TPU
 

Back to Top

duroloy pc/abs grades

key features

  • high impact resistance
  • high chemical resistance
  • easy to process
  • plating
  • gray
  • black
  • other colors available upon request
 

applications

  • mobile phone
  • computer
  • electronic
  • automotive

Back to Top

 

 

duroloy pc/abs grades:  overview

PROPERTIES METHOD UNIT AS-41 AS-61 AS-81 AH-61 AH-81

Melt Flow Rate

(260°C / 5.0 kg)

ASTM D-1238

ISO 1133

g/10 min 12 12 12 18 18
Specific Gravity

ASTM D-792

ISO 1183

g/cm3 1.10 1.13 1.15 1.13 1.15

Water Absorption

(in water for 24 hours at 23°C)

ASTM D-570 % 0.2 0.2 0.2 0.2 0.2
Mold Shrinkage ASTM D-955 % 0.55~0.75 0.55~0.75 0.55~0.75 0.55~0.75 0.55~0.75

Tensile Strength

(at break)

ASTM D-638

ISO R-527

MPa 44 47 53 49 53
kgf/cm2 450 480 540 500 540

Tensile Strength

(at yield)

ASTM D-638

ISO R-527

MPa 44 47 53 49 53
kgf/cm2 450 480 540 500 540
Tensile Modulus

ASTM D-638

ISO R-527

MPa 2200 2200 2200 2200 2200
kgf/cm2 22500 22500 22500 22500 22500

Elongation

(at break)

ASTM D-638

ISO R-527

% 65 110 130 110 110

Elongation

(at yield)

ASTM D-638

ISO R-527

% 5 5 5 5 5
Flexural Modulus

ASTM D-790

ISO 178

MPa 2300 2300 2300 2300 2300
kgf/cm2 23500 23500 23500 23500 23500

IZOD Impact Strength

(3.2 mm/Notched) at 23°C

ASTM D-256 J/m 390 470 600 440 540
kg.cm/cm 40 48 61 45 55

IZOD Impact Strength

(3.2 mm/Notched) at -30°C

ASTM D-256 J/m 300 400 420 310 390
kg.cm/cm 31 41 43 32 40

Deflection Temperature Under Load

(0.44 MPa; 3.2 mm)

ASTM D-648

ISO 75

°C 112 122 127 122 127

Deflection Temperature Under Load

(1.8 MPa; 3.2 mm)

ASTM D-648

ISO 75

°C 95 100 109 100 109

VICAT Softening Temperature

(50 N; 50 k/h)

ASTM D-1525

ISO 306

°C 113 118 133 118 128

VICAT Softening Temperature

(50N; 120 k/h)

ASTM D-1525

ISO 306

°C 115 120 135 120 130
Flammability UL94 - HB HB HB HB HB

 

Back to Top

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Last updated May 2007                                                                                                              Back to Top

 